Syntho SubseaLV

Cena: Zapraszamy do kontaktu z biurem

Syntho-Subsea™ LV is a unique blend of liquid epoxy, polymer, and aliphatic polyamine curing agents that is able to displace water from wet surfaces in order to make a permanent bond. The formulation is solvent-free to ensure safety and maximum technical performance. Kevlar® fibers are incorporated for reinforcement and viscosity management to achieve high-application rates – even subsea. Provides permanent protection under the most adverse conditions, the formula is uniquely field-friendly and uses advanced, low-toxicity ingredients in a high-build brushable/rollable product. This versatile epoxy system can achieve high-perfomance characteristics, excellent adhesion, resistance to high pressures, resistance to high and low temperature extremes, as well as outstanding resistance to petroleum products and chemical. This product can also be used for aboveground and belowground applications. Syntho-Subsea™ LV Epoxy can be shipped non-regulated by USDOT, IATA, and IMO.

Description

Syntho-Subsea™ LV is a unique blend of liquid epoxy, polymer, and aliphatic polyamine curing agents that is able to displace water from wet surfaces in order to make a permanent bond. The formulation is solvent-free to ensure safety and maximum technical performance. Kevlar® fibers are incorporated for reinforcement and viscosity management to achieve high-application rates – even subsea. Provides permanent protection under the most adverse conditions, the formula is uniquely field-friendly and uses advanced, low-toxicity ingredients in a high-build brushable/rollable product. This versatile epoxy system can achieve high-perfomance characteristics, excellent adhesion, resistance to high pressures, resistance to high and low temperature extremes, as well as outstanding resistance to petroleum products and chemical. This product can also be used for aboveground and belowground applications. Syntho-Subsea™ LV Epoxy can be shipped non-regulated by USDOT, IATA, and IMO.

Typical Applications:

  • Anticorrosive coating, including splash zone and subsea applications
  • Encapsulating coating.
  • Pipeline repair
  • Concrete repairs
  • Pipeline anomaly reinforcement and remediation
  • Brush or roller applied
  • All ISO 12944 environments (C1-C5M)

Benefits:

  • Use above- or below-grade, as well as immersion
  • Zero VOC system
  • Chemical resistant coating
  • Excellent abrasive resistance
  • Ships as non-hazardous by USDOT, IATA, and IMO
  • Fully cured in 24 hours

Technical data

Test Method Result
Tensile Strength ASTM D3039 6,000 psi (413.68 bar)
Compression Strength ASTM D695 7,380 psi (508.83 bar)
Flexural Strength ASTM D790 4,550 psi (313.71 bar)
Flexural Modulus ASTM D790 142,188 psi (9803.51 bar)
Lap Shear Strength ASTM D3163 1,782 psi (122.86 bar)
Abrasion Resistance CS17 wheels with 1,000 gram weights 34.0 mg/1,000 cycles

 

Cure Schedule:

Temperature Working Time Set Time
50°F (10°C) 225 minutes 24 hours
60°F (16°C) 150 minutes 12 hours
75°F (24°C) 75 minutes 4 hours
90°F (32°C) 35 minutes 2 hours

Measure Shore D hardness to confirm full set has been achieved before

Additional information

Packaging:

Produkt Opis
SUBLV04OZ 4 oz (197g) Bi-Pack
SUBLV080Z 8 oz (394g) Bi-Pack
SUBLV160Z 16 oz (787g) Bi-Pack
SUBLV02QT 2qt (1.8921) kit contents 1 qt A+1 qt B
SUBLV02G 2 gal (7.570I) kit contents 1 gal A+1 gal B
SUBLV10G 10 gal (37.8541) kit contents 5gal A+5gal B

 

Surface preparation:

Surface preparation and profiling shall promote continuous intimate contact between the CFRP system and pipe by providing a clean, smooth, and circumferential surface. Surface preparation shall be in accordance with SSPC-SP1 “Solvent Cleaning” and SSPC-SP10 / NACE 2 “Near White Blast Cleaning” 1-3 mil surface roughness (25-75 microns). If an exist-ing coating is present, roughen to degloss. The composite repair system is a bond -critical composite repair system requiring a strong adhesive bond between the clean pipe and the composite system.

Installation:

Installation of the composite System shall be performed by NRI qualified applicators only. Surface preparation, mixing of epoxy, and installation of the system are to be in accordance with NRI’s composite Installation Guide, latest revision. Quality control inspection during and after installation of the composite system shall be performed per NRI’s Installation Validation Procedure: Quality Control Records, latest revision.

Storage conditions:

Store in a cool, shaded area at an ambient temperature of 35ºC.

Datasheets

Datasheet – Syntho SubseaLV